Actividad antimicrobiana de adhesivo ortodóntico con nanopartículas de plata sobre Streptococcus mutans
Antimicrobial activity of orthodontic adhesive with silver nanoparticles on Mutans streptococci
Atividade antimicrobiana de adesivo ortodôntico com nanopartículas de prata sobre streptococcus mutans
Odontología (Ecuad.); 22 (2), 2020
Publication year: 2020
La aparatología fija usada en ortodoncia dificulta una adecuada higiene bucal, en estas condiciones el de-sarrollo de lesiones cariosas puede ser una complicación, uno de los principales agentes etiológicos involu-crados es Streptococcus mutans. La nanotecnología con plata tiene una aplicación preventiva importante en biomateriales dentales.
Objetivo:
Se determinó la actividad antimicrobiana sobre Streptococcus mutans de nanopartículas de plata (AgNPs) incluidas en adhesivos ortodónticos a diferentes concentraciones. Materia-les y métodos: En 20 cajas Petri con Streptococcus mutans inoculada en agar Müller-Hinton suplementado con 5% de sangre, se colocaron 6 discos de papel, 4 embe-bidos con AgNPs incluidas en un adhesivo orto-dóntico a concentraciones de 25, 75, 125 y 175 ppm, y 2 discos controles con clorhexidina al 0.12% y agua destilada. Se determinó la capacidad antimicrobiana en función de promedios de halos de inhibición a las 48 horas de incubación, en comparación con la escala de Duraffourd y la clorhexidina 0.12%.Resultados:
A 25 ppm no existió capacidad antibacteriana, a 75 ppm el 50% alcanzó sensibilidad límite, pero el 100% de las muestras a 125 y 175 ppm consiguieron sensibilidad límite, sin embargo, la clorhexidina al 0,12% presentó mayor sensibilidad entre media 60% y sumamente sensible 40%.Conclusión:
Las nanopartículas de plata con tamaño inferior a 100 nm, incluidas a 125 y 175 ppm en adhesivos de ortodoncia poseen actividad anti-microbiana sobre Streptococcus mutans, sin embargo, en el tiempo de estudio no alcanzan la sensibilidad de la clorhexidina al 0.12%.
The fixed appliances used in orthodontics make proper oral hygiene difficult, in these conditions the develop-ment of carious lesions can be a complication, one of the main etiologic agents involved is Mutans streptococci. It was determined that silver nanotechnology has an important preventive application in dental biomaterials.
Objective:
Antimicrobial activity on Mutans streptococci of silver nanoparticles (AgNPs) included in orthodon-tic adhesives at different concentrations.Materials and methods:
In 20 Petri dishes with Mutans streptococci inoculated in Müller-Hinton agar supplemented with 5% blood, 6 paper discs were placed, 4 soaked up with AgNPs included in an orthodontic adhesive at concentrations of 25, 75, 125 and 175 ppm, and 2 control discs with 0.12% chlorhexidine and distilled water. Antimicrobial capacity was determined based on averages of inhibition halos at 48 hours of incubation, compared to the Duraffourd scale and 0.12% chlorhexidine.Results:
At 25 ppm there was no antibacterial capacity, at 75 ppm 50% reached limit sensitivity, but 100% of the sam-ples at 125 and 175 ppm achieved limit sensitivity, however, chlorhexidine 0.12% showed higher sensitivity be-tween average 60% and highly sensitive 40%.Conclusión:
Silver nanoparticles smaller than 100 nm, included at 125 and 175 ppm in orthodontic adhessives, have antimicrobial activity on Strptococcus mutans, however, when studying, they don’t reach the sensitivity of chlorhexidine at 0.12%.
Os aparelhos fixos utilizados em ortodontia dificultam uma higiene bucal adequada, nessas condições o desenvolvimento de lesões cariosas pode ser uma complicação, um dos principais agentes etiológicos envol-vidos é o Streptococcus mutans. A nanotecnologia com partículas de prata tem uma importante aplicação pre-ventiva em biomateriais dentários.