Braz. dent. sci; 27 (2), 2024
Publication year: 2024
Objective:
This study aimed to evaluate the optical behavior of pressable lithia-silicate and lithia-zirconia-silicate glass ceramics toward additional heat treatment protocols. Material and Methods:
40 lithia-silicate discs (15mm x 1mm) were heat pressed following the manufacturers’ instructions. Discs were divided into four groups (n=10) according to type as follows: two groups of lithia-silicate-glass ceramics; Gp(E) (IPS e.max Press; Ivoclar Vivadent AG), Gp(L) (GC Initial LiSi Press, GC), two lithia-zirconia-silicate pressable glass ceramics; Gp(C) (Celtra Press, Dentsply Sirona) and Gp(A) (VITA Ambria, VITA Zahnfabrik). Each group was subdivided into (n=5): Subgroup(T1): the thermal tempering temperature was set 9% below the pressing temperature, Subgroup(T2): the temperature was set 5% below the pressing temperature. Optical properties:
color, translucency parameter (TP), and contrast ratio (CR) were evaluated by spectrophotometer (Aglient Cary 5000 UV-Vis–NIR) after pressing and after thermal tempering. Results:
Thermal tempering regardless of temperature resulted in a color shift within the acceptability level as ΔE for Gp(E) (3.18±2) followed by ΔE for Gp(L) (2.47±0.19) by ΔE for Gp(C) (2.26±0.14) and the last ΔE for Gp(A) (1.62±0.13). Subgroup(T2) showed a significantly higher color shift with mean ΔE(2.55±0.63) compared to Subgroup(T1) ΔE(2.35±0.59). There was a statistically significant increase in TP after tempering for all tested groups parallelled with a decrease in CR values. Conclusion:
Heat tempering of the tested lithia-silicate pressable ceramics had a significant effect on the optical outcome of these materials, being lithia-zirconia-silicate ceramics more stable and less affected optically than other lithia-silicate-glass ceramics.(AU)
Objetivo:
Avaliar o comportamento óptico de cerâmicas pressionáveis de vidro de litia-silicato e litia-zircônia-silicato sob protocolos adicionais de tratamento térmico. Materiais e métodos:
40 discos de litia-silicato (15mm x 1mm) foram prensados a quente conforme instruções dos fabricantes. Material e Métodos:
40 discos de litia-silicato (15mm x 1mm) foram prensados e divididos em quatro grupos (n=10): dois de lithia-silicato-vidro, Gp(E) (IPS e.max Imprensa) e Gp(L) (GC inicial LiSi Press), e dois de vidro prensado de litia-zircônia-silicato, Gp(C) (Celtra Press) e Gp(A) (VITA Ambria). Cada grupo foi subdividido em (n=5): Subgrupo(T1): amostras temperadas a 9% abaixo da temperatura de prensagem, e Subgrupo(T2): a temperatura foi ajustada 5% abaixo da temperatura de prensagem. As propriedades ópticas, incluindo cor, translucidez (TP) e contraste (CR), foram avaliadas com um espectrofotômetro (Aglient Cary 5000 UV-Vis-NIR) após prensagem e temperagem térmica. Resultados:
O tratamento térmico resultou em mudança de cor dentro do nível aceitável, com ΔE mais alto para Gp(E) (3,18±2), seguido por Gp(L) (2,47±0,19), Gp(C) (2,26±0,14), e Gp(A) (1,62±0,13). No subgrupo (T2), houve uma mudança de cor mais significativa, com ΔE médio de (2,55±0,63), comparado ao subgrupo (T1) com ΔE médio de (2,35±0,59). Houve aumento significativo na TP e redução nos valores de RC após o tratamento térmico em todos os grupos testados. Conclusão:
O tratamento térmico das cerâmicas prensadas de litia-silicato teve um efeito significativo na sua qualidade ótica, com as cerâmicas de litia-zircônia-silicato mostrando-se mais estáveis e menos afetadas visualmente em comparação com outras cerâmicas de litia-silicato-vidro(AU)