Introduction:
Light-cured resin cements are the first choice for the cementation of laminate veneers. Ideally, they should be biocompatible and offer minimum risks to patients. Objective:
The aim of this study was to evaluate, in vitro, the cytotoxicity of three resin cements: Variolink II, Ivoclar Vivadent (C1), Allcem Veneer, FGM (C2), and Rely X Veneer, 3M ESPE (C3). Material and method:
Twenty four samples of each of the cements were fabricated in a standardized metal mold, light activated, and transferred to a 96-well cell plate with culture of fibroblasts. After 24, 48, and 72h of incubation, cytotoxicity was assessed and cell viability was calculated by the methyl-thiazol-tetrazolium (MTT) colorimetric assay. Absorbance was measured at 570 nm using a microplate spectrophotometer. Result:
The following results were found: Variolink II presented viability of 72.24% (SD 6.80) after 24h, 83.92% (SD 5.26) after 48h, and 92.77% (SD 5.59) after 72h; Allcem Veneer exhibited viability of 70.46% (SD 12.91) after 24h, 85.03% (SD 21.4) after 48h, and 70.46% (SD 12.91) after 72h; Rely X Veneer showed viability of 5.06% (SD 0.88) after 24h, 5.84% (SD 1.18) after 48h, and 6.99% (SD 1.34) after 72h. Conclusion:
Under these testing conditions, Rely X Veneer presented significantly higher cytotoxicity compared with those of the other light-cured resin cements assessed.
Introdução:
Cimentos resinosos fotopolimerizáveis são materiais de eleição para a cimentação de facetas laminadas. Devem ser biocompatíveis oferencendo riscos mínimos ao uso clínico em pacientes. Objetivo:
O objetivo desse trabalho foi avaliar in vitro a citotoxicidade de três cimentos resinosos: Variolink II (Ivoclar Vivadent), Allcem Veneer, (FGM) e Rely X Veneer (3M ESPE). Material e método:
Vinte e quatro corpos de prova de cada cimento foram confeccionados em matrizes metálicas padronizadas e inseridos em placa de cultura de células de noventa e seis poços contendo fibroblastos da linhagem 3T3. As células foram cultivadas em meio de cultivo celular RPMI 1640 com 5% de soro fetal bovino, com 0,1% de penicilina/estreptomicina em estufa a 37◦C, em atmosfera úmida com 5% de CO2. O grau de citotoxicidade de cada cimento foi avaliado após os tempos de contato de 24h, 48h e 72h através do método MTT (3-(4,5-dimetiltiazol-2yl)-2,5- difenil brometo de tetrazolina), que avalia a viabilidade celular pela função mitocondrial. Após os tempos estabelecidos, as amostras foram removidas, tratadas e levadas ao espectofotômetro de microplaca para leitura da absorbância em 570nm. Resultado:
O cimento Variolink apresentou em 24h viabilidade de 72,24% (±6,80), em 48h de 83,92% (± 5,26) e de 92,77% (±5,59) em 72h. Allcem Veneer apresentou viabilidade de 70,46% (± 12,91) em 24h; 85,03% (± 21,4) em 48h e 70,46% (± 12,91) em 72h. O RelyX Veneer demonstrou viabilidade de 5,06% (± 0,88) em 24h; 5,84% (± 1,18) em 48h e 6,99% (± 1,34) em 72h. Conclusão:
Estes resultados demonstraram que o cimento Rely-X se apresentou significativamente mais citotóxico nas condições testadas.